Semiconductor device and method of manufacturing the same

ABSTRACT

To improve a reflow characteristic and realize leadlessness. A semiconductor device comprises a cross die pad which supports a semiconductor chip and in which an area of the region joined to the semiconductor chip is smaller than that of the outer size thereof being smaller than the rear surface of the semiconductor chip; wires connected to pads of the semiconductor chip; a plurality of inner leads which are arranged around the semiconductor chip and in which a silver plating layer is formed at a wire bonding area; molding resin for resin sealing the semiconductor chip; a plurality of outer leads exposed from the molding resin and in which a lead-free metallic layer is formed on a contact surface, wherein the flat surface size of the molding resin is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less, and thereby it is possible to improve a reflow characteristic and realize leadlessness.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a manufacturing technology of a semiconductor device, and more specifically, to a technology effectively applied to leadlessness of exterior solder plating in a semiconductor device having small die pad structure.

[0002] In an assembly process of a semiconductor package equipped with a semiconductor chip (semiconductor device), die bonding, wire bonding, resin sealing and the like are carried out one after another. Thereafter, in an exterior plating process, a tin (Sn)-lead (Pb) based solder layer is formed as exterior plating on a surface spot including a contact portion (surface to be packaged) of a substrate of a lead (hereinafter referred to as an outer lead) that is not sealed with molding resin in order to be packaged onto a printed circuit board or a circuit board.

[0003] However, there is a demand for a countermeasure against an environmental issue these years, and especially with regard to lead (Pb), as pointed out in Japanese Patent Laid-Open No. 5-270860, it is demanded to reduce lead to an appropriate level even in a generally electronic part such as a semiconductor device, and a packaging board and the like, from a environmental viewpoint.

[0004] Thereupon, as solder which replaces tin (Sn)-lead (Pb) based solder, such a proposal has been made in, for example, Japanese Patent Laid-Open No. 10-93004, No. 11-179586, No. 11-221694, No. 11-330340 and the like.

[0005] First, in Japanese Patent Laid-Open No. 10-93004, an invention using tin (Sn)-bismuth (Bi) based solder as lead-free solder which replaces tin-lead based solder has been proposed, and a technology for making solder connection easier has been described by forming a tin-bismuth based alloy layer on an external connection electrode lead wire of an electronic parts.

[0006] Further, in Japanese Patent Laid-Open No. 11-179586, a technology for ensuring sufficient connection strength by use of Sn—Ag—Bi based solder has been proposed as lead-free solder which replaces tin-lead based solder.

[0007] Additionally, in Japanese Patent Laid-Open No. 11-221694, a technology for improving reliability of a connection portion by use of Sn—Ag—Bi—In based solder has been proposed as lead-free solder which replaces tin-lead based solder.

[0008] Also, in Japanese Patent Laid-Open No. 11-330340, a semiconductor device in which an Sn—Bi based plating film is formed on a lead has been introduced, and a technology for preventing occurrence of cracks and being capable of a solder connection with a high degree of reliability has been proposed.

[0009] In the case where Sn—Pb eutectic substitutional lead-free solder is employed in exterior plating, an Sn base alloy is selected according to applications, and especially in car packaging parts, eminently developing mobile electronic equipments and highly reliable parts, an alloy that is excellent in join strength and in heat resistant fatigue characteristics is desired. As an Sn base alloy that is excellent in join strength and in heat resistant fatigue characteristics and regards high reliability as an important thing, an Sn—Ag based alloy is known, and the fusion point of Sn—Pb eutectic solder is generally 183° C. while the fusion point of most of Sn—Ag based alloys appears 200° C. or more, the temperature of which is higher than the fusion point of the Sn—Pb eutectic solder.

[0010] Therefore, at present, a reflow temperature in packaging a semiconductor integrated circuit by use of Sn—Pb eutectic substitutional lead-free solder becomes high inevitably. Thereupon, the present inventors have packaged a semiconductor integrated circuit device in which an inner lead is Ag plated and an outer lead is plated at a reflow temperature higher than the conventional reflow temperature by use of lead-free substitutional solder whose the fusion point is higher than that of Sn—Pb eutectic solder, and have conducted evaluations thereof. As a result, it has been found that product failures are caused due to wire disconnection.

[0011] As a countermeasure of such wire disconnection, the present applicant has thought that hard palladium (pd) plating is performed onto a wire joining portion of an inner lead and thereby the thickness of a join root portion of a wire is ensured to increase the join strength, as shown in Japanese Patent Application No. 2000-46724.

[0012] However, there is a problem that the palladium plating increases in cost.

[0013] Note that, in the above-mentioned four references, there are not a description that in the case of using lead-free solder for leadlessness, the reflow temperature becomes high and thereby the reflow margin of the semiconductor device becomes small, and a description about the countermeasure thereof.

[0014] An object of the present invention is planrovide a semiconductor device and a method of manufacturing the semiconductor device, which improve a reflow characteristic and realizes leadlessness.

[0015] Another object of the present invention is planrovide a semiconductor device and a method of manufacturing the semiconductor device, which suppress increase in cost to realize leadlessness.

[0016] The above-mentioned and other objects and novel features of the present invention will become apparent from the present description in conjunction with the appended drawings.

SUMMARY OF THE INVENTION

[0017] Outline of representative ones of the inventions disclosed in the present application will be briefly explained as below.

[0018] The present invention includes a semiconductor chip mounting portion in which an area of the region joined to a semiconductor chip is smaller than that of the rear surface of the semiconductor chip; a plurality of inner leads in which a silver plating layer is formed on a wire bonding area; molding resin for resin sealing the semiconductor chip; a plurality of outer leads in which a lead-free metallic layer is formed on a contact surface thereof, and is an LQFP or a TQFP in which the flat surface size of the molding resin is formed to be equal to or less than 28 mm×28 mm.

[0019] Further, the outlines of other inventions of the present application will be briefly described in classification into sections hereinafter.

[0020] 1. A semiconductor device comprises:

[0021] a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0022] a wire connected to a surface electrode of said semiconductor chip;

[0023] a plurality of inner leads expanding around said semiconductor chip, wherein a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0024] a molding resin for resin sealing said semiconductor chip; and

[0025] a plurality of outer leads connected to the inner leads and protruding from the molding resin, in which a lead-free metallic layer is formed on a contact surface,

[0026] wherein said semiconductor device is a QFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less.

[0027] 2. A semiconductor device comprises:

[0028] a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0029] a wire connected to a surface electrode of said semiconductor chip;

[0030] a plurality of inner leads expanding around said semiconductor chip, wherein a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0031] a molding resin for resin sealing said semiconductor chip; and

[0032] a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface,

[0033] wherein said semiconductor device is one of an LQFP and a TQFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm.

[0034] 3. A semiconductor device comprises:

[0035] a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0036] wires connecting to surface electrodes of the semiconductor chip;

[0037] a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0038] molding resin for resin sealing said semiconductor chip; and

[0039] a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface,

[0040] wherein said semiconductor device is a QFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less.

[0041] 4. A semiconductor device comprises:

[0042] a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0043] a wire connecting to a surface electrode of said semiconductor chip;

[0044] a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0045] molding resin for resin sealing said semiconductor chip; and

[0046] a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface,

[0047] wherein said semiconductor device is one of a QFP, an LQFP and a TQFP, the QFP being formed such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm.

[0048] 5. A semiconductor device comprises:

[0049] a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0050] a wire connecting to a surface electrode of said semiconductor chip;

[0051] a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0052] molding resin for resin sealing said semiconductor chip; and

[0053] a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface,

[0054] wherein said semiconductor device is one of a QFP, an LQFP and a TQFP, the QFP being formed such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm.

[0055] 6. A semiconductor device comprises a QFN, said QFN including:

[0056] a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0057] a wire connected to a surface electrode of said semiconductor chip;

[0058] a plurality of inner leads arranged around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined;

[0059] molding resin for resin sealing said semiconductor chip; and

[0060] a plurality of outer leads arranged to be exposed to a circumferential portion of a surface located in a packaging side of said molding resin, in which a lead-free metallic layer is formed on a contact surface.

[0061] 7. A semiconductor device comprises a QFN, said QFN including:

[0062] a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip;

[0063] a wire connecting to a surface electrode of said semiconductor chip;

[0064] a plurality of inner leads arranged around said semiconductor chip, in which a silver plating layer is formed at wire bonding area to which said wire is joined;

[0065] molding resin for resin sealing said semiconductor chip; and

[0066] a plurality of outer leads arranged to be exposed to a circumferential portion of a surface located in a packaging side of said molding resin, in which a lead-free metallic layer is formed on a contact surface.

[0067] 8. A method of manufacturing a semiconductor device, comprises the steps of:

[0068] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface;

[0069] mounting said semiconductor chip onto said die pad via a die bonding material;

[0070] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0071] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and

[0072] separating said plurality outer leads protruding from said molding resin, from a frame portion of said lead frame,

[0073] wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.

[0074] 9. A method of manufacturing a semiconductor device, comprises the steps of:

[0075] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface;

[0076] mounting said semiconductor chip onto said die pad via a die bonding material;

[0077] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0078] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and

[0079] separating said plurality of outer leads protruding from said molding resin, from a frame portion of said lead frame,

[0080] wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being forming such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed such that the flat surface size of the molding resin is equal to or less than 20 mm×20 mm.

[0081] 10. A method of manufacturing a semiconductor device, comprises the steps of:

[0082] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at a wire bonding area, and a plurality of outer lead portions in which a lead-free metallic layer is formed on a contact surface continuing on said inner lead portions;

[0083] mounting said semiconductor chip onto said die pad via a die bonding material;

[0084] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode;

[0085] forming molding resin by resin molding said semiconductor chip such that said lead-free metallic layer of each of said plurality of outer lead portions is exposed to a circumferential portion thereof; and

[0086] separating said plurality of outer lead portions from a frame portion of said lead frame,

[0087] wherein a QFN is assembled.

[0088] 11. A method of manufacturing a semiconductor device, comprises the steps of:

[0089] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface;

[0090] mounting said semiconductor chip onto said die pad via a die bonding material;

[0091] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0092] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and

[0093] separating said plurality of outer leads protruding from said molding resin, from a frame portion of said lead frame,

[0094] wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.

[0095] 12. A method of manufacturing a semiconductor device, comprises the steps of:

[0096] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said inner leads and in which a lead-free metallic layer is formed on a contact surface;

[0097] mounting said semiconductor chip onto said cross die pad via a die bonding material;

[0098] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0099] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and

[0100] separating said plurality of outer leads protruding from said molding resin, from a frame portion of said lead frame;

[0101] wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being forming such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed such that the flat surface size of the molding resin is equal to or less than 20 mm×20 mm.

[0102] 13. A method of manufacturing a semiconductor device, comprises the steps of:

[0103] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at a wire bonding area, and a plurality of outer lead portions which are continued to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface;

[0104] mounting said semiconductor chip onto said cross die pad via a die bonding material;

[0105] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode;

[0106] forming molding resin by resin molding said semiconductor chip such that said lead-free metallic layer of each of said plurality of outer lead portions is exposed to a circumferential portion thereof; and

[0107] separating said plurality of outer lead portions from a frame portion of said lead frame,

[0108] wherein a QFN is assembled.

[0109] 14. A method of manufacturing a semiconductor device, comprises the steps of:

[0110] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads;

[0111] mounting said semiconductor chip onto said die pad via a die bonding material;

[0112] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0113] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude;

[0114] forming a lead-free metallic layer on a contact surface of said plurality of outer leads protruding from said molding resin; and

[0115] separating said plurality of outer leads from a frame portion of said lead frame,

[0116] wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.

[0117] 15. A method of manufacturing a semiconductor device, comprising the steps of:

[0118] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said inner leads;

[0119] mounting said semiconductor chip onto said die pad via a die bonding material;

[0120] connecting, by a wire, a surface electrodes of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0121] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude;

[0122] forming a lead-free metallic layer on a contact surface of each of said plurality of outer leads protruding from said molding resin; and

[0123] separating said plurality of outer leads from a frame portion of said lead frame;

[0124] wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being formed such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm.

[0125] 16. A method of manufacturing a semiconductor device, comprises the steps of:

[0126] preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at wire bonding area, and a plurality of outer lead portions connected to said inner leads;

[0127] mounting said semiconductor chip onto said die pad via a die bonding material;

[0128] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode;

[0129] forming molding resin by resin molding said semiconductor chip such that said plurality of outer lead portions is exposed to a circumferential portion of a surface located in a packaging side;

[0130] forming a lead-free metallic layer on the contact surface of said plurality of outer lead portions exposed to said molding resin; and

[0131] separating said plurality of outer lead portions from a frame portion of said lead frame,

[0132] wherein a QFN is assembled.

[0133] 17. A method of manufacturing a semiconductor device, comprises the steps of:

[0134] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads;

[0135] mounting said semiconductor chip onto said die pad via a die bonding material;

[0136] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0137] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude;

[0138] forming a lead-free metallic layer on each contact surface of said plurality of outer lead portions protruding from said molding resin; and

[0139] separating said plurality of outer leads from a frame portion of said lead frame,

[0140] wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.

[0141] 18. A method of manufacturing a semiconductor device, comprises the steps of:

[0142] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads;

[0143] mounting said semiconductor chip onto said cross die pad via a die bonding material;

[0144] connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode;

[0145] forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protruded;

[0146] forming a lead-free metallic layer on each contact surface of said plurality outer lead portions protruding from said molding resin; and

[0147] separating said plurality of outer leads from a frame portion of said lead frame,

[0148] wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being formed such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm.

[0149] 19. A method of manufacturing a semiconductor device, comprises the steps of:

[0150] preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at a wire bonding area, and a plurality of outer lead portions connected to said inner lead portions;

[0151] mounting said semiconductor chip onto said cross die pad via a die bonding material;

[0152] connecting, by a wire, a surface electrodes of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode;

[0153] forming molding resin by resin molding said semiconductor chip such that said plurality of outer lead portions are exposed to a circumferential portion of a surface located in a packaging side;

[0154] forming a lead-free metallic layer on each contact surface of said plurality of outer lead portions exposed to said molding resin; and

[0155] separating said plurality of outer lead portions from a frame portion of said lead frame,

[0156] wherein a QFN is assembled.

BRIEF DESCRIPTION OF THE DRAWINGS

[0157]FIG. 1 is a plan view showing the structure of a QFP serving as one example of a semiconductor device that is an embodiment of the present invention.

[0158]FIG. 2 is a cross-sectional view showing the structure of the QFP shown in FIG. 1.

[0159]FIG. 3 is a partially plan view showing one example of the structure of a lead frame used in assembly of the QFP shown in FIG. 1.

[0160]FIG. 4 is a partially enlarged plan view showing the structure of a cross die pad serving as a semiconductor chip mounting portion of the lead frame shown in FIG. 3.

[0161]FIG. 5 is a partially plan view showing one example of the structure in which a silver plating layer and an exterior plating layer are formed on the lead frame shown in FIG. 3.

[0162]FIG. 6 is a partially enlarged plan view showing one example of the structure obtained at the time when a double-sided adhesive tape is attached to the cross die pad shown in FIG. 4.

[0163]FIG. 7 is a partially enlarged plan view showing a structure obtained when a double-sided adhesive tape that is a modification of the double-sided adhesive tape shown in FIG. 6 is attached.

[0164]FIG. 8 is a partially enlarged plan view showing a structure obtained when a double-sided adhesive tape that is a modification of the double-sided adhesive tape shown in FIG. 6 is attached.

[0165]FIG. 9 is a partially plan view showing the structure obtained after die bonding in the assembly of the QFP shown in FIG. 1.

[0166]FIG. 10 is a partially enlarged cross-sectional view showing a sectional structure taken along line A-A shown in FIG. 9.

[0167]FIG. 11 is a partially enlarged cross-sectional view showing the structure of a die bonding condition using a double-sided adhesive tape that is a modification, relative to the die bonding condition shown in FIG. 10.

[0168]FIG. 12 is a partially enlarged cross sectional view showing the structure of a die bonding condition using molding resin paste and a single-sided adhesive tape modified, relative to the die bonding condition shown in FIG. 10.

[0169]FIG. 13 is a partially plan view showing the structure obtained after wire bonding in the assembly of the QFP shown in FIG. 1.

[0170]FIG. 14 is a partially plan view showing the structure obtained after wire bonding in the assembly using a small size semiconductor chip relative to the lead frame shown in FIG. 13.

[0171]FIG. 15 is a partially cross-sectional view showing one example of the structure obtained at resin molding in the assembly of the QFP shown in FIG. 1.

[0172]FIG. 16 is a partially plan view showing one example of the structure obtained after resin molding in the assembly of the QFP shown in FIG. 1.

[0173]FIG. 17 is a side view showing one example of the structure after cutting and formation in the assembly of the QFP shown in FIG. 1.

[0174]FIG. 18 is a partially enlarged cross-sectional view showing one example of the structure obtained at the time when exterior plating of an outer lead of the QFP is carried out after resin molding.

[0175]FIG. 19 is a relational view showing relations between each semiconductor device and molding resin thickness in the embodiment of the present invention.

[0176]FIG. 20 is a comparative view showing a technical concept of the semiconductor device according to the embodiment of the present invention.

[0177]FIG. 21 is a diagram showing the results of wire crack inspected relative to the size and thickness of a molding resin portion in the semiconductor device according to the embodiment of the present invention.

[0178]FIG. 22 is a partially plan view showing one example of the structure of a multiple lead frame used in the assembly of the QFP shown in FIG. 1.

[0179]FIG. 23 is a partially cross-sectional view showing one example of the structure obtained at die bonding in the assembly of the QFP shown in FIG. 1.

[0180]FIG. 24 is a partially cross sectional view showing one example of the structure obtained at wire bonding in the assembly of the QFP shown in FIG. 1.

[0181]FIG. 25 is a partially cross-sectional view showing one example of the structure obtained at cutting and formation in the assembly of the QFP shown in FIG. 1.

[0182]FIG. 26 is a partially plan view showing the structure of a die pad of a lead frame that is a modification, relative to the lead frame shown in FIG. 3.

[0183]FIG. 27 is a partially plan view showing the structure of a die pad of a lead frame that is a modification, relative to the lead frame shown in FIG. 3.

[0184]FIG. 28 is a partially plan view showing the structure of a die pad of a lead frame that is a modification, relative to the lead frame shown in FIG. 3.

[0185]FIG. 29 is a partially plan view showing the structure of a die pad of a lead frame that is a modification, relative to the lead frame shown in FIG. 3.

[0186]FIG. 30 is a plan view showing the structure of QFP to be assembled by use of the lead frame that is a modification and is shown in FIG. 26.

[0187]FIG. 31 is a cross-sectional view showing the structure of the QFP in FIG. 30.

[0188]FIG. 32A is a view showing the structure of a QFN serving as a semiconductor device that is other embodiment of the present invention, and is a cross-sectional view.

[0189]FIG. 32B is a view showing the structure of a QFN serving as a semiconductor device that is other embodiment of the present invention, and is a bottom surface view.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0190] In the embodiments described below, the invention will be described in a plurality of sections or embodiments when required as a matter of convenience. However, these sections or embodiments are not irrelevant to each other unless otherwise stated, and the one relates to the entire or a part of the other as a modification example, details, a supplementary explanation or the like thereof.

[0191] Also, in the embodiments described below, when referring to the number of elements (including number of pieces, values, amounts, ranges, or the like), the number of elements is not limited to a specific number unless otherwise stated, or except the case where the number is apparently limited to a specific number in principle, or the like. The number larger or smaller than the specified number is also applicable.

[0192] Further, in the embodiments described below, it goes without saying that the components (including element steps or the like) are not always essential unless otherwise stated, or except the case where the components are apparently essential in principle, or the like.

[0193] Similarly, in the embodiments described below, when the shape of the components and the like, or the positional relation and the like thereof, or the like are mentioned, the substantially approximate and similar shapes and the like are included therein unless otherwise stated, or except the case where it can be conceived that they are apparently excluded in principle, or the like. This condition is also applicable to the numerical value and the range described above.

[0194] The embodiments of the present invention will be described hereinafter in detail with reference to the drawings. Also, components having the same functions are denoted by the same reference symbols throughout the drawings for describing the embodiments, and the repetitive description thereof will be omitted.

[0195]FIG. 1 is a plan view showing the structure of a QFP serving as one example of a semiconductor device that is an embodiment of the present invention; FIG. 2 is a cross-sectional view showing the structure of the QFP shown in FIG. 1; FIG. 3 is a partially plan view showing one example of the structure of a lead frame used in assembly of the QFP shown in FIG. 1; FIG. 4 is a partially enlarged plan view showing the structure of a cross die pad serving as a semiconductor chip mounting portion of the lead frame shown in FIG. 3; FIG. 5 is a partially plan view showing one example of the structure in which a silver plating layer and an exterior plating layer are formed on the lead frame shown in FIG. 3; FIG. 6 is a partially enlarged plan view showing one example of the structure obtained at the time when a double-sided adhesive tape is attached to the cross die pad shown in FIG. 4; FIG. 7 and FIG. 8 are partially enlarged plan views each showing a structure obtained when a double-sided adhesive tape that is a modification of the double-sided adhesive tape shown in FIG. 6 is attached; FIG. 9 is a partially plan view showing the structure obtained after die bonding in the assembly of the QFP shown in FIG. 1; FIG. 10 is a partially enlarged cross-sectional view showing a sectional structure taken along line A-A shown in FIG. 9; FIG. 11 is a partially enlarged cross-sectional view showing the structure of a die bonding condition using a double-sided adhesive tape that is a modification, relative to the die bonding condition shown in FIG. 10; FIG. 12 is a partially enlarged cross sectional view showing the structure of a die bonding condition using molding resin paste and a single-sided adhesive tape modified, relative to the die bonding condition shown in FIG. 10; FIG. 13 is a partially plan view showing the structure obtained after wire bonding in the assembly of the QFP shown in FIG. 1; FIG. 14 is a partially plan view showing the structure obtained after wire bonding in the assembly using a small size semiconductor chip relative to the lead frame shown in FIG. 13; FIG. 15 is a partially cross-sectional view showing one example of the structure obtained at resin molding in the assembly of the QFP shown in FIG. 1; FIG. 16 is a partially plan view showing one example of the structure obtained after resin molding in the assembly of the QFP shown in FIG. 1; FIG. 17 is a side view showing one example of the structure after cutting and formation in the assembly of the QFP shown in FIG. 1; FIG. 18 is a partially enlarged cross-sectional view showing one example of the structure obtained at the time when exterior plating of an outer lead of the QFP is carried out after resin molding; FIG. 19 is a relational view showing relations between each semiconductor device and molding resin thickness in the embodiment of the present invention; FIG. 20 is a comparative view showing a technical concept of the semiconductor device according to the embodiment of the present invention; FIG. 21 is a diagram showing the results of wire crack inspected relative to the size and thickness of a molding resin portion in the semiconductor device according to the embodiment of the present invention; FIG. 22 is a partially plan view showing one example of the structure of a multiple lead frame used in the assembly of the QFP shown in FIG. 1; FIG. 23 is a partially cross-sectional view showing one example of the structure obtained at die bonding in the assembly of the QFP shown in FIG. 1; FIG. 24 is a partially cross sectional view showing one example of the structure obtained at wire bonding in the assembly of the QFP shown in FIG. 1; and FIG. 25 is a partially cross-sectional view showing one example of the structure obtained at cutting and formation in the assembly of the QFP shown in FIG. 1.

[0196] A semiconductor device that is an embodiment of the present invention is a molding resin sealed type formed by molding and is a surface packaging type, and has the size (flat surface size and thickness) of molding resin 3 within a predetermined range. As one example of such a semiconductor device, a QFP (Quad Flat Package) 6 shown in FIG. 1 will be taken up and explained hereinafter.

[0197] In reference to FIG. 1 to FIG. 5, a structure of the QFP 6 will be explained hereinafter. The QFP comprises a cross die pad 1 g which supports a semiconductor chip 2 and which is smaller in outer size than a rear surface 2 b opposite to a semiconductor die surface 2 c of the semiconductor chip 2; wires 4 connected to pads 2 a that are surface electrodes of the semiconductor chip 2; a plurality of inner leads 1 b which extends around the semiconductor chip 2 and in which silver plating layers 1 a are formed at wire bonding areas 1 j to which the wires 4 are joined; molding resin 3 that is a resin sealing portion formed by resin molding the semiconductor chip 2 and the wires 4; a plurality of outer leads 1 c which is connected to the inner leads 1 b and protruding from the molding resin 3 in four directions and in which a lead-free metallic layer 1 m is formed, as exterior plating, at least on a contact surface 1 connected to a packaging board such as a printed wiring board. Also, the QFP 6 is an LQFP (Low profile Quad Flat package) or a TQFP (Thin Quad Flat Package) in which the flat surface size (P×Q shown in FIG. 1) of the molding resin 3 is formed to be equal to or less than 28 mm×28 mm, or is one in which the flat surface size of the molding resin 3 is formed to be equal to or less than 28 mm×28 mm and which the thickness (T shown in FIG. 2) thereof is formed to be 1.4 mm or less.

[0198] Further, the QFP 6 may be formed such that the flat surface size of the molding resin 3 is equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, or may be such an LQFP or a TQFP that the flat surface size of the molding resin 3 is formed to be equal to or less than 20 mm×20 mm.

[0199] Note that, the structures of the LQFP and the TQFP are the same as that of the QFP 6 shown in FIG. 1 and FIG. 2, and, as shown in FIG. 19, by EIAJ Standards (Standards of Electronic Industries Association of Japan), the molding resin thickness (thickness of the molding resin 3) of each semiconductor device is defined and thereby the QFP 6, LQFP, TQFP, and a QFN (Quad Flat Non-leaded Package) 17 shown in FIG. 32 are classified.

[0200] In the present embodiment, attention is paid to the size (molding resin amount depending on the flat surface size and thickness) of each molding resin 3 of semiconductor devices having the QFP structure and the QFN structure, and, as shown in FIG. 19, by EIAJ Standards, especially by the molding resin thickness, the QFP 6 (molding resin thickness of 2.0 mm or more), the LQFP (molding resin thickness of 1.4 mm), the TQFP (molding resin thickness of 1.0 mm) and the QFN 17 (molding resin thickness of 0.45 to 2.50 mm) are classified, respectively.

[0201] Herein, an allowable range of the size of the molding resin 3 of the QFP 6 according to the present embodiment will be explained.

[0202] First, the QFP 6 according to the present embodiment is for realizing leadlessness of solder when packaged. Note that the reflow temperature becomes high in a leadless state, and so the molding resin amount at resin sealing increases in the semiconductor device whose the molding resin 3 is large, and accordingly molding resin stress also increases and the margin of each wire to wire cracks (including also wire disconnection) decreases.

[0203] Thereupon, in order to stabilize each wire relative to the wire cracks, palladium (Pd) plating is carried out on each wire bonding area 1 j of the inner leads 1 b, and thereby the joint strength between each wire 4 and each inner lead 1 b is enhanced and occurrence of the wire cracks can be prevented.

[0204] However, since use of the palladium (Pd) plating requires high costs, in the QFP 6 of the present embodiment a low cost silver (Ag) plating layer 1 a is formed on each wire bonding area 1 j of the inner leads 1 b as shown in FIG. 2.

[0205] Therefore, the size of the molding resin 3 is limited and the molding resin amount is set small, and thereby the molding resin stress is reduced at high temperature reflow and the wire cracks and wire disconnection are prevented.

[0206] Note that, in order to realize leadlessness of solder in being packaged, the lead-free metallic layer 1 m which is an exterior plating is formed on a surface including at least the contact surface 1 of each outer lead 1 c protruding from the molding resin 3.

[0207] Also, in leadlessness, there arises a problem of molding resin cracks as the reflow temperature becomes high. However, herein by employing the small cross die pad 1 g whose a mounting portion (semiconductor chip mounting portion) has a smaller area than the rear surface 2 b of the semiconductor chip 2 and by making part of the rear surface 2 b of the semiconductor chip 2 being close to the molding resin of the molding resin 3, the close characteristic between the semiconductor chip 2 to be mounted and the molding resin 3 is increased, and the reflow characteristic is enhanced to realize leadlessness.

[0208] Accordingly, in the comparative view of the technical concepts shown in FIG. 20, use of the technical range corresponding to the lower left ones surrounded by a dashed line among four squares achieves leadlessness.

[0209] Note that the cross die pad 1 g is a semiconductor chip mounting portion provided at a crossing position of two suspension leads 1 n.

[0210] In the QFP 6, FIG. 20 shows the results obtained by evaluating wire cracks (including also wire disconnection) and cost using, as parameters, a large or small size (a much or little molding resin amount) of the molding resin 3 and the plating kind (Ag plating or Pb plating) of each wire bonding area 1 j of the inner leads 1 b.

[0211] Like the lower left squares shown in FIG. 20, only in the case where the molding resin amount is made little (the size of the molding resin 3 is made large) and the silver plating layer 1 a is formed on each wire bonding area 1 j of the inner leads 1 b, both items of wire crack and cost each have a circle symbol, and this condition has been taken into the technical concept of the present embodiment.

[0212] Further, about a semiconductor device having the conventional QFP structure in which the silver plating layer la is formed on each wire bonding area 1 j of the inner leads 1 b and each wire 4 is joined to each silver plating layer 1 a, FIG. 21 is the results obtained by inspecting wire cracks (including also wire disconnection) with using, as parameters, the length of a side of each silver plating layer 1 a and the molding resin thickness, on the predetermined condition (that the semiconductor device is left in an atmosphere having a temperature of 85° C. and a humidity of 85% for 48 hours and thereafter infrared ray reflow for 10 seconds at 260° C. is carried out three times).

[0213] According to this, all the results when inspected are good each have a circle if the length of one side of the molding resin 3 (the length P or Q shown in FIG. 1) is 28 mm or less and the molding resin thickness is 1.4 mm or less.

[0214] Further, all test pieces were evaluated as preferable (o) if the length of one side of the molding resin 3 was set 20 mm or less, and the molding resin thickness was set 3.0 mm or less.

[0215] As a consequence, it is preferable that the allowable range of the size of the molding resin 3 in the QFP structure of this embodiment may fall within the case where the length of one side of the molding resin 3 is 28 mm or less and the molding resin thickness is 1.4 mm or less, or the case where the length of one side of the molding resin 3 is 20 mm or less and the molding resin thickness is 3.0 mm or less.

[0216] Note that a raw material for a lead frame used in the inspection shown in FIG. 21 is general one such as an iron-nickel alloy or a copper alloy or the like.

[0217] Further, the wires 4 employed in the inspection are gold wires whose each wire diameter is 30 μm.

[0218] Thereby, in the QFP 6 (including an LQFP and a TQFP) of the present embodiment, it is preferable to use a lead frame formed by a raw material such as an iron-nickel alloy, a copper alloy, or the like as the lead frame 1 shown in FIG. 3 and FIG. 22.

[0219] Further, it is preferable to use gold wires as the wires 4.

[0220] Also, the molding resin 10 which is shown in FIG. 15 and is seal molding resin for forming the molding resin 3 is, for instance, thermosetting epoxy resin.

[0221] Note that the outer leads 1 c are formed in a gull wing shape, and, as shown in FIG. 18, a lead-free metallic layer 1 m as exterior plating of lead-free solder is formed on each surface thereof. Each of these lead free metallic layers 1 m is a solder plating layer whose a fusion point is higher than that of tin-lead eutectic solder, and is, for example, an alloy obtained by adding either copper (Cu) or bismuth (Bi), or copper and bismuth to an Sn—Ag based metal.

[0222] However, each lead-free metallic layer is not limited to the above-mentioned alloy, and an alloy of Zn, In, or Sb or the like, and Sn or an Sn based alloy may be employed too.

[0223] Also, a die bonding material used for fixing the semiconductor chip 2 onto the cross die pad 1 g is, for example, molding resin paste such as silver paste 8 or the like shown in FIG. 2 and FIG. 10. However, in the case of the cross die pad 1 g, since a join area of the semiconductor chip 2 is small, a double-sided adhesive tape 5 as an adhesive tape shown in FIGS. 6 to 8 and FIG. 11 may be employed singly in order to reinforce the join strength of the semiconductor chip 2.

[0224] The double-sided adhesive tape 5 may be such a cross shape as to match the shape of the cross die pad 1 g as shown in FIG. 6, or may be a thin rectangle as shown in FIG. 7, or further, as shown in FIG. 8, may be employed by attaching a plurality of small double-sided adhesive tapes 5 onto one cross die pad 1 g, and the shape thereof and the number of tape pieces to be attached are not limited specifically.

[0225] Note that, as shown in FIG. 11, the double-sided adhesive tape 5 comprises a base film 5 a such as polyamide tape or the like and adhesive layers 5 b arranged on both of front and rear sides thereof. However, in the place of this double-sided adhesive tape 5, as shown in FIG. 12, a single-sided adhesive tape 7 comprising a tape base 5 a and an adhesive layer 5 b may be employed to laminate and combine this single-sided adhesive tape 7 and molding resin paste such as silver paste 8 or the like.

[0226] As mentioned above, by using an adhesive tape such as a double-sided adhesive tape 5, a single-sided adhesive tape 7 or the like as a die bonding material, it is possible to enhance the adhesion between the semiconductor chip mounting portion such as the cross die pad 1 g or the like and the semiconductor chip 2, and thereby to suppress occurrence of molding resin cracks even in the case of a semiconductor device having a small semiconductor chip mounting portion such as the cross die pad 1 g and so on.

[0227] Note that, in the semiconductor chip 2, a desired semiconductor integrated circuit is formed on the semiconductor die surface 2 c thereof, and bonding pads 2 a formed on this semiconductor die surface 2 c and the inner leads 1 b corresponding thereto are connected through the wires 4, and further the outer leads 1 c linked to the inner leads 1 b are output to the outside of the molding resin 3 as external terminals of the QFP6.

[0228] Therefore, the transmission of signals between the semiconductor chip 2 and the outer leads 1 c is made via the wires 4 and the inner leads 1 b.

[0229] According to the QFP 6 (including an LQFP and a TQFP) of this embodiment, the size of the molding resin 3 is set such that the length of one side of the molding resin 3 is 28 mm or less and the molding resin thickness is 1.4 mm or less, or that the length of one side of the molding resin 3 is 20 mm or less and the molding resin thickness is 3.0 mm or less, and further the cross die pad 1 g smaller in area than the rear surface 2 b of the semiconductor chip 2 is packaged on the semiconductor chip 2 and the lead-free metallic layer 1 m as exterior plating is formed on the outer leads 1 c. Therefore, it is possible to improve a reflow characteristic (namely, it is possible to increase the margin of a reflow characteristic).

[0230] As a result, it is possible to use high fusion point solder and to realize leadlessness.

[0231] Moreover, the silver plating layer 1 a is formed on each wire bonding area 1 j of the inner leads 1 b without using palladium (Pb) plating, and therefore the cost can be suppressed and leadlessness can be realized.

[0232] Therefore, according to the QFP 6 (including an LQFP and a TQFP) of the present embodiment, it is possible to realize leadlessness without the occurrence of molding resin cracks and wire cracks (including wire disconnection and wire peeling-off).

[0233] Further, since the occurrence of molding resin cracks and wire cracks is suppressed, it is possible to enhance the reliability of the semiconductor device (the QFP 6).

[0234] Furthermore, by adopting the cross die pad 1 g smaller in area than the rear surface 2 b of the semiconductor chip 2, the semiconductor chips 2 having a plurality of sizes can be packaged relative to one kind of lead frame 1, and consequently it is possible to reduce the number of kinds of lead frame 1.

[0235] As a result, it is possible to achieve the standardization of the lead frame 1.

[0236] Next, a method of manufacturing the QFP 6 according to the present embodiment will be explained.

[0237] Note that the case will be explained where manufacture is carried out by employing, as the lead frame 1 to be used in the manufacturing method of the QFP 6, the lead frame 1 shown in FIG. 22 in which a plurality of units using, as a unit, a package body 1 h shown in FIG. 3 is arranged in a raw.

[0238] However, the lead frame 1 may use a matrix frame in which one package body 1 h is arranged in matrix arrangement of plural lines×plural rows, too.

[0239] First, the lead frame 1 is prepared which has the cross die pad 1 g that is shown in FIG. 4 and that is a cross die pad smaller in outer size than the rear surface 2 b of the semiconductor chip 2; a plurality of inner leads 1 b in which the silver plating layer 1 a is formed at each wire bonding area 1 j located near tips thereof; and a plurality of outer leads 1 c that is connected to the inner leads 1 b and in which a lead-free metallic layer 1 m is formed at least on the contact surfaces 1.

[0240] Note that, herein, explanation will be made of the case where in each package body 1 h of the lead frame 1, as shown in FIG. 5, the silver plating layer 1 a (hatched portions in FIG. 5) is formed in advance on each wire bonding area 1 j of the inner leads 1 b, and the lead-free metallic layer 1 m (hatched portion in FIG. 5) is formed on a surface including the contact surface 1 in the area corresponding to each outer lead 1 c. However, the lead-free metallic layer 1 m may not be formed in prior to assembly. In this case, the following assembly is executed in this order: after molding, the lead-free metallic layer 1 m is formed on each outer lead 1 c protruding from the molding resin 3; and thereafter cutting and formation is carried out.

[0241] Also, in each package body 1 h, a suspension lead 1 n for supporting the cross die pad 1 g; a plurality of inner leads 1 b extending in four directions around the cross die pad 1 g; and the outer leads 1 c serving as external terminals and formed integrally with each inner lead; and dam bars 1 i for preventing molding resin (molding resin 10 shown in FIG. 15) from flowing out in molding are arranged. Each outer lead 1 c is supported by frame portions 1 f sectioning each package body 1 h.

[0242] Further, on each of these frame portions 1 f, a locating hole 1 d and a pilot hole 1 e for transferring the lead frame 1 in die bonding and wire bonding are formed.

[0243] Note that, in FIG. 3, the portion corresponding to a lower left suspension lead 1 n among four suspension leads 1 n becomes a molding gate 1 t in molding.

[0244] Subsequently, when molding resin paste such as silver paste 8 or the like is used as a die bonding material, an appropriate amount of silver paste 8 is applied onto a die pad 1 p of each cross die pad 1 g by potting or the like.

[0245] However, when an adhesive tape such as the double-sided adhesive tape 5 shown in FIGS. 6 to 8 or FIG. 11, the single-sided adhesive tape 7 shown in FIG. 12, or the like is used without using the molding resin paste as a die bonding material, the above-mentioned adhesive tape may be in advance attached onto the die pad 1 p of the cross die pad 1 g in each package body 1 h of the lead frame 1 in start of assembly or the above-mentioned adhesive tape may be attached in start of die bonding process.

[0246] Thereafter, in each package body 1 h, as shown in FIG. 23, die bonding (also referred to as pellet bonding or chip mounting) is carried out to mount the semiconductor chip 2 onto the cross die pad 1 g via a die bonding material (silver paste 8) by use of a collet 12.

[0247] Namely, the rear surface 1 b of the semiconductor chip 2 and the die pad 1 p of the cross die pad 1 g are jointed via the die bonding material consisting of molding resin paste or an adhesive tape or the both.

[0248] At this time, as shown in FIG. 23, first the cross die pad 1 g of the lead frame 1 is arranged onto a stage 11 of a die bonder, and then the semiconductor chip 2 is sucked and held by the collet 12, and thereby the semiconductor chip 2 is moved.

[0249] Then, the semiconductor chip 2 is lowered by the collet 12 and the semiconductor chip 2 is arranged onto the cross die pad 1 g. By adding a slight load from the collet 12 onto the semiconductor chip 2 and giving heat to the semiconductor chip 2 from the stage 11 via the cross die pad 1 g, the semiconductor chip 2 is fixed via the die bonding material such as silver paste 8 or the like, as shown in FIG. 9 and FIG. 10.

[0250] Thereafter, as shown in FIG. 2, the bonding pads 2 a of the semiconductor chip 2 and the inner leads 1 b corresponding thereto are connected by wire bonding.

[0251] Namely, wire bonding is carried out by use of the bonding wires 4 such as gold wires or the like, and thereby the bonding pads 2 a of the semiconductor chip 2 and the wire bonding areas 1 j of the inner leads 1 b corresponding thereto are connected with the wires 4.

[0252] At this time, as shown in FIG. 24, the semiconductor chip 2 is placed on the stage 13 of the wire bonder, and, first, connection to each wire 4 in a side of the semiconductor chip 2 is carried out by a capillary 14 as first bonding, and thereafter connection between each wire 4 and each wire bonding area 1 j of the inner leads 1 b is carried out as second bonding.

[0253] This operation, as shown in FIG. 13, is carried out onto each bonding pad 2 a shown in FIG. 24 and located on the semiconductor die surface 2 c of the semiconductor chip 2 one after another.

[0254] Note that, since the silver plating layer 1 a as shown in FIG. 2 and FIG. 5 is formed on each wire bonding area 1 j of each inner lead 1 b, the wires 4 of gold wires and the silver plating layer 1 a are connected and thereby the connection strength between the wires 4 and the inner leads 1 b can be enhanced.

[0255] Also, as shown in FIG. 14, even in the case of using a small semiconductor chip 2 which has been shrunk and thereby comes to a small size, the wire length becomes long but the wire bonding can be carried out.

[0256] After completion of wire bonding, the semiconductor chip 2 and the cross die pad 1 g and the wires 4 and respective inner leads 1 b are resin sealed by a molding method, and thereby the molding resin 3 is formed as shown in FIG. 16.

[0257] Note that molding resin (molding resin 10 shown in FIG. 15) to be used in the above-mentioned molding is, for example, epoxy based thermosetting resin or the like.

[0258] At this time, as shown in FIG. 2, the semiconductor chip 2 of the lead frame 1 and the wires 4 are arranged onto a cavity 18 a of a molding die 18 shown in FIG. 15 such that a plurality of outer leads 1 c in which a lead-free metallic layer 1 m is formed on the contact surface 1 protrude from the molding resin 3. Thereafter, closing is carried out, and molding resin 10 is injected into the cavity 18 a and resin molded.

[0259] Note that, in this embodiment, an LQFP or a TQFP in which the flat surface size of the molding resin 3 is formed to be equal to or less than 28 mm×28 mm, or the QFP 6 in which the flat surface size of the molding resin 3 is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less is assembled.

[0260] This is determined according to the size (size in flat surface direction and depth) of the cavity 18 a of the molding die 18 for forming the molding resin 3, and so the shape and depth of the cavity 18 a are set such that the molding resin 3 is formed according to the size thereof.

[0261] Further, the QFP 6 may be formed such that the flat surface size of the molding resin 3 is formed to be equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, or an LQFP or a TQFP may be formed such that the flat surface size of the molding resin 3 is formed to be equal to or less than 20 mm×20 mm. Accordingly, molding is variously carried out by use of the molding die 18 having the cavity 18 a corresponding to the size of this molding resin 3.

[0262] Note that, in each package body 1 h of the lead frame 1 shown in FIG. 3, the molding resin 3 is formed in the inside area of each dam bar 1 i as shown in FIG. 16.

[0263] After completion of resin sealing, a plurality of outer leads 1 c protruding from the molding resin 3 is cut and removed from the respective frame portions 1 f of the lead frame 1 by use of a die or the like for cutting and formation.

[0264] At that time, as shown in FIG. 25, by use of the above-mentioned die 16 for cutting and formation and a stamping die 15, the outer leads 1 c are bent and cut (separated from the frame portions 1 f), and then the outer leads 1 c are bent and formed in a gull wing shape.

[0265] Thereby, it is possible to manufacture the QFP 6 (semiconductor device) shown in FIG. 17, and the lead-free metallic layer 1 m is formed at least on the contact surface 1 (in this case the whole surface) of each outer lead 1 c in this QFP 6.

[0266] Note that, in the case of assembly made by use of the lead frame 1 in which the lead-free metallic layer 1 m is not formed on a surface including the contact surface 11 of an area corresponding to each outer lead 1 c at the start of assembly, molding is performed and thereafter the lead-free metallic layer 1 m is formed on each of the outer leads 1 c protruding from the molding resin 3, and then cutting and formation are carried out to have the shape shown in FIG. 18.

[0267] The invention made by the present inventors has been explained in detail according to the embodiments of the invention. However, the present invention is not limited to the above-mentioned embodiments, and, needless to say, may be variously changed and modified without departing from the sprit thereof.

[0268] For example, in the above-mentioned embodiments, the case has been described where the semiconductor chip mounting portion supported by the suspension leads 1 n is the cross die pad 1 g smaller in outer size than the rear surface 2 b of the semiconductor chip 2. However, it is preferable that the above-mentioned semiconductor chip mounting portion may be smaller in outer size than the rear surface 2 b of the semiconductor chips 2, and some modifications of such semiconductor chip mounting portion are shown in FIG. 26 to FIG. 29, and these modifications are referred to as small die pads 1 q.

[0269] First, the small die pad 1 q shown in FIG. 26 is formed in a small circular shape.

[0270] Namely, the die pad 1 p thereof is formed in a small circular shape.

[0271] Further, the small die pad 1 q shown in FIG. 27 is formed in a small square shape.

[0272] While, the small circular die pad 1 q shown in FIG. 28 is formed in such a shape as to combine the small die pad 1 q having a small circle shape as shown in FIG. 26 and the cross die pad 1 g shown in FIG. 3.

[0273] Further, the small die pad 1 q shown in FIG. 29 is formed in such a shape as to provide islands 1 r outside the circular small die pad 1 q of each suspension lead 1 n, and thereby it is possible to stably mount various sizes of the semiconductor chip 2.

[0274] Note that one example of the QFP 6 assembled by use of the lead frame 1 having modifications of the small die pad 1 q shown in FIG. 26 to FIG. 29 is illustrated in FIG. 30 and FIG. 31.

[0275] Even the QFP 6 shown in FIG. 30 and FIG. 31 and incorporating the small die pad 1 q therein can obtain the same effects as the QFP 6 having the small die pad 1 g according to the above-mentioned embodiment.

[0276] Further, the small die pad 1 q, similarly to the case of the cross die pad 1 g, may be applied even to an LQFP and a TQFP.

[0277] Also, in the above-mentioned embodiments, the case has been described where the semiconductor device is the QFP 6, the LQFP or the TQFP. However, the semiconductor device may also be the QFN 17 as shown in other embodiments of FIGS. 32A and 32B.

[0278] Namely, the QFN 17 includes a small die pad 1 q (or a cross die pad 1 g) smaller in outer size than the semiconductor chip 2; a plurality of inner lead portions is in which the silver plating layer 1 a is formed on each wire bonding area 1 j; and a plurality of outer lead portions 1 k arranged so as to be exposed to the circumferential portion of the rear surface (surface of a packaging side) 3 a of the molding resin 3, and forming the lead-free metallic layer 1 m on the contact surface 11.

[0279] Even the case of the QFN 17 mentioned above can be obtain the same effects as the QFP 6 taken out of the above-mentioned embodiment.

[0280] The effects obtained by the representative ones among the inventions disclosed in this application will be briefly explained as below.

[0281] (1) The size of the molding resin is set such that the length of one side of the molding resin is 28 mm or less and the molding resin thickness is 1.4 mm or less, or the length of one side of the molding resin is 20 mm or less and the molding resin thickness is 3.0 mm or less. Further, the semiconductor chip is mounted on the cross die pad or the small die pad and the lead-free metallic layer is formed on each of the outer leads. Thereby, it is possible to improve a reflow characteristic and realize leadlessness.

[0282] (2) The silver plating layer in the place of palladium plating is formed on the wire bonding area of the inner leads, and thereby it is possible to suppress the cost and realize leadlessness. 

What is claimed is:
 1. A semiconductor device comprising: a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connected to a surface electrode of said semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; a molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is one of an LQFP and a TQFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm.
 2. A semiconductor device comprising: a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connected to a surface electrode of said semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; a molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to the inner leads and protruding from the molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is a QFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less.
 3. A semiconductor device comprising: a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connected to a surface electrode of said semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; a molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is one of an LQFP and a TQFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm.
 4. A semiconductor device comprising: a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; wires connecting to surface electrodes of the semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is a QFP in which the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm and the thickness thereof is formed to be 1.4 mm or less.
 5. A semiconductor device comprising: a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connecting to a surface electrode of said semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is one of a QFP, an LQFP and a TQFP, the QFP being formed such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm.
 6. A semiconductor device comprising: a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connecting to a surface electrode of said semiconductor chip; a plurality of inner leads expanding around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; molding resin for resin sealing said semiconductor chip; and a plurality of outer leads connected to said inner leads and protruding from said molding resin, in which a lead-free metallic layer is formed on a contact surface, wherein said semiconductor device is one of a QFP, an LQFP and a TQFP, the QFP being formed such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm and the thickness thereof is formed to be 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is formed to be equal to or less than 20 mm×20 mm.
 7. A semiconductor device comprising a QFN, said QFN including: a die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connected to a surface electrode of said semiconductor chip; a plurality of inner leads arranged around said semiconductor chip, in which a silver plating layer is formed at a wire bonding area to which said wire is joined; molding resin for resin sealing said semiconductor chip; and a plurality of outer leads arranged to be exposed to a circumferential portion of a surface located in a packaging side of said molding resin, in which a lead-free metallic layer is formed on a contact surface.
 8. A semiconductor device comprising a QFN, said QFN including: a cross die pad supporting a semiconductor chip and being smaller in outer size than the surface opposite to the semiconductor die surface of said semiconductor chip; a wire connecting to a surface electrode of said semiconductor chip; a plurality of inner leads arranged around said semiconductor chip, in which a silver plating layer is formed at wire bonding area to which said wire is joined; molding resin for resin sealing said semiconductor chip; and a plurality of outer leads arranged to be exposed to a circumferential portion of a surface located in a packaging side of said molding resin, in which a lead-free metallic layer is formed on a contact surface.
 9. The semiconductor device according to claim 1, wherein said lead-free metallic layer is a solder plating layer having a fusion point higher than tin-lead eutectic solder.
 10. The semiconductor device according to claim 5, wherein a double-sided adhesive tape is provided as a die bonding material for fixing said semiconductor chip to one of said die pad and said cross die pad.
 11. The semiconductor device according to claim 7, wherein an adhesive tape and molding resin paste to be laminated thereon are provided as a die bonding material for fixing said semiconductor chip to one of said die pad and said cross die pad.
 12. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and separating said plurality outer leads protruding from said molding resin, from a frame portion of said lead frame, wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.
 13. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed on a wire bonding area, and a plurality of outer leads which are connected to said respective inner leads and in which a lead-free metallic layer is formed on a contact surface; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude in which said lead-free metallic layer is formed on the contact surface; and separating said plurality of outer leads protruding from said molding resin, from a frame portion of said lead frame, wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.
 14. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at a wire bonding area, and a plurality of outer lead portions in which a lead-free metallic layer is formed on a contact surface continuing on said inner lead portions; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said lead-free metallic layer of each of said plurality of outer lead portions is exposed to a circumferential portion thereof; and separating said plurality of outer lead portions from a frame portion of said lead frame, wherein a QFN is assembled.
 15. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude; forming a lead-free metallic layer on a contact surface of said plurality of outer leads protruding from said molding resin; and separating said plurality of outer leads from a frame portion of said lead frame, wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.
 16. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said inner leads; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrodes of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude; forming a lead-free metallic layer on a contact surface of each of said plurality of outer leads protruding from said molding resin; and separating said plurality of outer leads from a frame portion of said lead frame; wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being formed such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm.
 17. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at wire bonding area, and a plurality of outer lead portions connected to said inner leads; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer lead portions is exposed to a circumferential portion of a surface located in a packaging side; forming a lead-free metallic layer on the contact surface of said plurality of outer lead portions exposed to said molding resin; and separating said plurality of outer lead portions from a frame portion of said lead frame, wherein a QFN is assembled.
 18. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads; mounting said semiconductor chip onto said die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protrude; forming a lead-free metallic layer on each contact surface of said plurality of outer lead portions protruding from said molding resin; and separating said plurality of outer leads from a frame portion of said lead frame, wherein the flat surface size of said molding resin is formed to be equal to or less than 28 mm×28 mm, and thereby one of an LQFP and a TQFP is assembled.
 19. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner leads in which a silver plating layer is formed at a wire bonding area, and a plurality of outer leads connected to said respective inner leads; mounting said semiconductor chip onto said cross die pad via a die bonding material; connecting, by a wire, a surface electrode of said semiconductor chip and said silver plating layer of said wire bonding area in said inner leads corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer leads protruded; forming a lead-free metallic layer on each contact surface of said plurality outer lead portions protruding from said molding resin; and separating said plurality of outer leads from a frame portion of said lead frame, wherein one of a QFP, an LQFP and a TQFP is assembled, the QFP being formed such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm and the thickness thereof is 3 mm or less, and the LQFP and the TQFP being formed respectively such that the flat surface size of said molding resin is equal to or less than 20 mm×20 mm.
 20. A method of manufacturing a semiconductor device, comprising the steps of: preparing a lead frame having a cross die pad smaller in outer size than the surface opposite to the semiconductor die surface of a semiconductor chip, a plurality of inner lead portions in which a silver plating layer is formed at a wire bonding area, and a plurality of outer lead portions connected to said inner lead portions; mounting said semiconductor chip onto said cross die pad via a die bonding material; connecting, by a wire, a surface electrodes of said semiconductor chip and said silver plating layer of said wire bonding area in said inner lead portions corresponding to the surface electrode; forming molding resin by resin molding said semiconductor chip such that said plurality of outer lead portions are exposed to a circumferential portion of a surface located in a packaging side; forming a lead-free metallic layer on each contact surface of said plurality of outer lead portions exposed to said molding resin; and separating said plurality of outer lead portions from a frame portion of said lead frame, wherein a QFN is assembled. 